문제1
Cracks formed by carbonate stress corrosion are best detected:
Cracks formed by carbonate stress corrosion are best detected:
정답: B
설명: (ITDumpsKR 회원만 볼 수 있음)
문제2
(What nondestructive examination (NDE) technique requires the least amount of surface preparation to locate wet H#S damage mechanisms?)
(What nondestructive examination (NDE) technique requires the least amount of surface preparation to locate wet H#S damage mechanisms?)
정답: C
설명: (ITDumpsKR 회원만 볼 수 있음)
문제3
(What is the minimum pH value where chloride stress corrosion cracking begins to occur?)
(What is the minimum pH value where chloride stress corrosion cracking begins to occur?)
정답: A
설명: (ITDumpsKR 회원만 볼 수 있음)
문제4
(The signature mark of a mechanical fatigue failure is a "clam shell" type fingerprint:)
(The signature mark of a mechanical fatigue failure is a "clam shell" type fingerprint:)
정답: A
설명: (ITDumpsKR 회원만 볼 수 있음)
문제5
Short-term stress rupture is a/an:
Short-term stress rupture is a/an:
정답: D
설명: (ITDumpsKR 회원만 볼 수 있음)
문제6
Damage from oxidation is usually determined by:
Damage from oxidation is usually determined by:
정답: A
설명: (ITDumpsKR 회원만 볼 수 있음)
문제7
Hydrogen stress cracking is normally found in:
Hydrogen stress cracking is normally found in:
정답: B
설명: (ITDumpsKR 회원만 볼 수 있음)
문제8
What type of damage is affected by higher hydrogen partial pressures?
What type of damage is affected by higher hydrogen partial pressures?
정답: D
설명: (ITDumpsKR 회원만 볼 수 있음)
문제9
Which of the following is a contributing factor in caustic corrosion?
Which of the following is a contributing factor in caustic corrosion?
정답: B
설명: (ITDumpsKR 회원만 볼 수 있음)
문제10
(A section of vacuum bottom outlet piping is being replaced because of naphthenic acid corrosion (NAC).
Which of the following potential replacement materials would be most resistant to NAC?)
(A section of vacuum bottom outlet piping is being replaced because of naphthenic acid corrosion (NAC).
Which of the following potential replacement materials would be most resistant to NAC?)
정답: B
설명: (ITDumpsKR 회원만 볼 수 있음)
문제11
Amine stress corrosion cracking is most likely to occur in what services?
Amine stress corrosion cracking is most likely to occur in what services?
정답: B
설명: (ITDumpsKR 회원만 볼 수 있음)
문제12
In a wet H2S-type environment, what fluid material will significantly increase the probability of blistering?
In a wet H2S-type environment, what fluid material will significantly increase the probability of blistering?
정답: D
설명: (ITDumpsKR 회원만 볼 수 있음)
문제13
Polythionic acid stress corrosion cracking (PTASCC) can be detected by:
Polythionic acid stress corrosion cracking (PTASCC) can be detected by:
정답: C
설명: (ITDumpsKR 회원만 볼 수 있음)
문제14
How can temper embrittlement be prevented if a material contains critical levels of the appropriate impurity elements and is exposed in the embrittling temperature range?
How can temper embrittlement be prevented if a material contains critical levels of the appropriate impurity elements and is exposed in the embrittling temperature range?
정답: D
설명: (ITDumpsKR 회원만 볼 수 있음)
문제15
(An equipment component made of 1-1/4 Cr-1/2 Mo steel that has lost ductility due to temper embrittlement would be susceptible to further damage by which of the following mechanisms?)
(An equipment component made of 1-1/4 Cr-1/2 Mo steel that has lost ductility due to temper embrittlement would be susceptible to further damage by which of the following mechanisms?)
정답: A
설명: (ITDumpsKR 회원만 볼 수 있음)